聚硅氧烷丙烯酸酯聚氨酯三元复合乳液的制备及表征
关键词: 水性聚氨酯 丙烯酸酯 聚硅氧烷 甲基丙烯酸甘油酯
类 别: 涂料与助剂 >> 涂料
来 源: 第二届全国涂料科学与技术会议
资料类型: pdf文件
资料大小: 436K
简 介: Isophorone diisocyanate was reacted with bis(3-(1-methoxy-2- hydroxypropoxy) propyl) terminated polysiloxanes (PMTS) to input cyanate group in polysiloxanes molecular chains. Polypropylene and dimethylol propanic acid were then added to
get polysiloxane modified polyurethane (PSU) prepolymer. Dihydroxyl glyceryl methacrylate was then used as coupling agent to react with PSU prepolymers to introduce vinyl groups with objective to conduct graft-polymerization with acrylics in a subsequent step, and so that to get polysiloxane acrylic modified polyurethane (PSU-AC) latexes. The results showed that the particle size, surface tension and viscosity of the PSU-AC latexes were kept constant with increase in PMTS content, while contact angle of
PSU-AC film with water increased. When PMTS was less than 10% (based on PSU), PSU-AC loss tanδ exhibited two peaks with varying temperature. When PMTS content was higher than 10%, the loss tanδ exhibited just one peak, but it was much wider than the two observed with PMTS below 10%. Without PMTS, acrylics polyurethane film became white after it was immerged in water for 11 h, and this whitening effect was observed upon 36 h immersion in water when 2.5% and 5.0% of PMTS were incorporated in PSU-AC. While when PMTS was more than 7.5%, PSU-AC film showed no visible change after immersion in water for 15 days.
上传人: panwang
上传时间: 2010-09-20 14:01:06
下载次数: 1
消耗积分: 4
我要收藏:
 
友情提示:下载后对该资源进行评论,即可奖励2分。
好:
中:
差:
本栏目部分资源来自互联网,仅为促进数据共享和信息交流,如有版权问题请告知本网或上传者本人,本网会及时给予答复。
报告错误  1.下载无效  2. 资料明显无价值  3. 资料重复存在
评论:(共有0人发表评论) 更多>>
你还没有登录,无法发表评论,请首先